What precautions should be paid attention to in the use of safety steel mesh: first, in the construction process of steel mesh, the surface or sharp edge of the mesh should be too rough; during the process of loading and unloading steel mesh, the construction personnel should pay attention to safety protection.

　　钢筋网片如果放置太久了，施工的时候要进行除锈处理，如果网片周围有严重的腐蚀性酸、碱烟雾时候不能施工，要排除。

　　If the reinforcing steel mesh is placed too long, it should be rust removed during construction. If there is serious corrosive acid and alkali smoke around the mesh, it should be eliminated.

　　钢筋网片在收受到很大冲击，发生严重变形、搭接处脱开，则要修理或更换，不可勉强使用。

　　Reinforcement mesh is greatly impacted in receiving, serious deformation occurs, and the lap is detached. It should be repaired or replaced, and can not be used reluctantly.

　　顽皮受到脏物污染或网上嵌入砂浆、泥灰粒及其它可能引起磨损的异物时，应进行冲洗，自然干燥后再用。

　　When naughty is contaminated by dirt or embedded in mortar, mortar and other foreign bodies which may cause wear and tear on the net, it should be washed and used after natural drying.

　　钢筋网片在出口时要求都比较严格，钢筋网片镀锌一般分为两种形式来做，一种是采用镀锌丝来焊接、另一种是用黑丝（或者冷轧带肋钢筋）焊接完成后，经过镀锌厂镀锌完成，出口钢筋网片多采用后者，也就是先焊后镀，这种工艺效果好，焊点牢固。

　　Steel mesh is strictly required when exporting. Galvanizing of steel mesh is generally divided into two forms. One is to use galvanized wire to weld, the other is to use black wire (or cold-rolled ribbed steel bar) to weld, and then finish galvanizing in galvanizing plant. The latter is usually used for exporting steel mesh, that is, welding before plating. This process has good effect and solder joint is firm.

　　很少的直接是不经过镀锌处理就直接出口的。

　　Very few of them are exported directly without galvanizing treatment.

　　在生产网片时往往会遇到是否留毛边和无毛边问题，出口大部分是不留毛边的，极少情况也有留毛边。

　　In the production of mesh, we often encounter the problem of whether or not to leave the wool edge and no wool edge. Most of the exports do not leave the wool edge, and very few cases also have the wool edge.

　　还有需要注意的就是热镀锌钢筋网片的上锌量比较高一般可以达到250g使用年限长、不易腐蚀生锈，质量比较高、焊接点比较牢固、外形美观，所以一般出口比较多，具体规格根据客户的要求定做。

　　It should also be noted that the zinc content of hot-dip galvanized steel mesh is relatively high, which can generally reach 250g long service life, not easy to corrode and rust, high quality, solder joint is relatively strong, beautiful appearance, so there are more general exports, specific specifications are customized according to customer requirements.